Regardons rapidement la chambre de cyclage de température et le choc de température
Jusqu’à présent, il y a encore beaucoup de gens qui pensent que l’application du test de choc de température et du test de cycle de température est similaire, car les gens ne connaissent pas assez les différences entre les deux équipements de test, et les considèrent même comme le même test, si vous lisez cet article pensez également qu’il n’y a pas de différence entre le choc de température et le cycle de température, alors vous avez tort.
Choc thermique
Choc thermique test, known as high and low temperature shock test, cold and thermal impact test, is used to test the degree of material structure or composite material that can be tolerated under the continuous environment of extremely high temperature and extremely low temperature in an instant, so as to test chemical changes or physical damage caused by thermal expansion or contraction in a short time. The temperature impact test chamber has a temperature change rate greater than 10 degrees/minute, and the heating/cooling rate is not less than 30C/ minute. The temperature change range is large, and the test severity also increases with the increase of the temperature change rate
.jpg)
The difference between temperature impact test chamber and Temperature cycling chamber is mainly due to the different stress loading mechanism. The temperature shock test mainly examines the failure caused by creep and fatigue damage, while the Temperature cycling test mainly examines the failure caused by shear fatigue. Choc thermique test allows the use of two tank test equipment; The temperature cycle test was carried out with a single tank test device. The temperature change rate in the second tank should be greater than 50 ° C /min. Therefore, the most fundamental difference between the Temperature cycling test and the temperature shock test is that the temperature conversion is carried out at a constant rate
Dans des circonstances normales, si le taux de changement dépasse 5 °C/min, il peut être considéré comme un test de changement rapide de température. Le choc de température consiste à réaliser l’échange de régions à haute température et à basse température dans un temps spécifié. La méthode d’essai générale exige que le temps de commutation de la zone de température soit inférieur à 20 S. La température de sortie de la chambre d’essai peut être stabilisée en 5 minutes et la température de l’échantillon peut être stabilisée en 15 minutes. Il peut simuler avec précision des environnements naturels complexes tels que basse température, haute température, haute température et humidité élevée, basse température et faible humidité. Il convient aux tests de fiabilité des plastiques, de l’électronique, de l’alimentation, de l’habillement, des véhicules, des métaux, des produits chimiques, des matériaux de construction et d’autres industries.
La chambre d’essai du cycle de température peut fournir un environnement à haute température et à forte humidité pour comparer les changements de matériau et le fort degré de réduction de la décomposition du caoutchouc et du plastique avant et après l’essai ; Il peut également simuler l’environnement du conteneur pour détecter la décoloration et le rétrécissement du caoutchouc et du plastique à haute température et humidité.
L’équipement est conçu pour tester la résistance à la chaleur, au froid et à l’humidité de divers matériaux.
Le choc thermique est principalement utilisé dans le test de chaleur du four et le test de chauffage du test de performance de sécurité de la batterie, mais par rapport à la chambre d’essai du cycle de température, la chambre d’essai de choc thermique n’a pas d’humidité.
Choc thermique
Choc thermique test, known as high and low temperature shock test, cold and thermal impact test, is used to test the degree of material structure or composite material that can be tolerated under the continuous environment of extremely high temperature and extremely low temperature in an instant, so as to test chemical changes or physical damage caused by thermal expansion or contraction in a short time. The temperature impact test chamber has a temperature change rate greater than 10 degrees/minute, and the heating/cooling rate is not less than 30C/ minute. The temperature change range is large, and the test severity also increases with the increase of the temperature change rate
.jpg)
Test de cycle de température
Test de cycle de température is also known as thermal cycle test, high and low temperature cycle test, that is, the test sample is exposed to a preset high and low temperature alternating test environment. In order to avoid the impact of temperature shock, the temperature change rate during the test must be less than 20℃/ min. At the same time, in order to achieve the effect of creep and fatigue damage, it is recommended that the test temperature cycle is 25℃~100℃, or it can also use a cycle test of 0℃~100℃ according to the use of the product, and the exposure time is 15 minutes.The difference between temperature impact test chamber and Temperature cycling chamber is mainly due to the different stress loading mechanism. The temperature shock test mainly examines the failure caused by creep and fatigue damage, while the Temperature cycling test mainly examines the failure caused by shear fatigue. Choc thermique test allows the use of two tank test equipment; The temperature cycle test was carried out with a single tank test device. The temperature change rate in the second tank should be greater than 50 ° C /min. Therefore, the most fundamental difference between the Temperature cycling test and the temperature shock test is that the temperature conversion is carried out at a constant rate
Dans des circonstances normales, si le taux de changement dépasse 5 °C/min, il peut être considéré comme un test de changement rapide de température. Le choc de température consiste à réaliser l’échange de régions à haute température et à basse température dans un temps spécifié. La méthode d’essai générale exige que le temps de commutation de la zone de température soit inférieur à 20 S. La température de sortie de la chambre d’essai peut être stabilisée en 5 minutes et la température de l’échantillon peut être stabilisée en 15 minutes. Il peut simuler avec précision des environnements naturels complexes tels que basse température, haute température, haute température et humidité élevée, basse température et faible humidité. Il convient aux tests de fiabilité des plastiques, de l’électronique, de l’alimentation, de l’habillement, des véhicules, des métaux, des produits chimiques, des matériaux de construction et d’autres industries.
La chambre d’essai du cycle de température peut fournir un environnement à haute température et à forte humidité pour comparer les changements de matériau et le fort degré de réduction de la décomposition du caoutchouc et du plastique avant et après l’essai ; Il peut également simuler l’environnement du conteneur pour détecter la décoloration et le rétrécissement du caoutchouc et du plastique à haute température et humidité.
L’équipement est conçu pour tester la résistance à la chaleur, au froid et à l’humidité de divers matériaux.
Le choc thermique est principalement utilisé dans le test de chaleur du four et le test de chauffage du test de performance de sécurité de la batterie, mais par rapport à la chambre d’essai du cycle de température, la chambre d’essai de choc thermique n’a pas d’humidité.